Synthesis and Sensing Response of Magnesium Antimoniate Oxide (MgSb2O6) in the Presence of Propane Atmospheres at Different Operating Voltages.

Nanoparticles of MgSb2O6 were synthesized using a microwave-assisted wet chemistry method, followed by calcination at 700 °C. Their ability to detect different concentrations of propane gas (C3H8) at various operating voltages was evaluated. The material's crystalline phase was identified using X-ray powder diffraction (XRD). The morphology was analyzed by scanning electron microscopy (SEM), finding bar- and polyhedron-type geometries. Through transmission electron microscopy (TEM), we found particle sizes of 8.87-99.85 nm with an average of ~27.63 nm. Employing ultraviolet-visible (UV-Vis) spectroscopy, we found a band gap value of ~3.86 eV. Thick films made with MgSb2O6 powders were exposed to atmospheres containing 150, 300, 400, and 600 ppm of propane gas for dynamic testing. The time-dependent sensitivities were ~61.09, ~88.80, ~97.65, and ~112.81%. In addition, tests were carried out at different operating voltages (5-50 V), finding very short response and recovery times (~57.25 and ~18.45 s, respectively) at 50 V. The excellent dynamic response of the MgSb2O6 is attributed mainly to the synthesis method because it was possible to obtain nanometric-sized particles. Our results show that the trirutile-type oxide MgSb2O6 possesses the ability, efficiency, and thermal stability to be applied as a gas sensor for propane.

Treatment of tequila vinasse and elimination of phenol by coagulation-flocculation process coupled with heterogeneous photocatalysis using titanium dioxide nanoparticles.

In this research, we are reporting the treatment of tequila vinasse by a coagulation-flocculation process coupled with heterogeneous photocatalysis using two types of titanium dioxide nanoparticles, i.e. (1) commercial nanoparticles, and (2) nanoparticles synthesized by sol-gel. The efficiency in the elimination of phenol, which is one of the most harmful contaminants in tequila vinasse, was also included in the evaluation of the treatment process. The synthesized titanium dioxide nanoparticles were annealed in air at 400°C for 1 h and were characterized by X-ray diffraction, transmission electron microscopy, ultraviolet-visible and Raman spectroscopy. Anatase phase was observed in both samples, with a crystallite size of 22.5 and 9.8 nm for commercial and synthesized nanoparticles respectively. Tequila vinasse was characterized before and after the treatments by measuring physicochemical parameters such as pH, chemical oxygen demand (COD), colour, total suspended solids (TSS), as well as using ultraviolet-visible spectroscopy and Raman spectroscopy to identify the presence of organic compounds, and gas chromatography (GC) for phenol quantification. Raw vinasse was treated initially by coagulation-flocculation producing clarified vinasse, which in turn was treated by photocatalysis for 3 h using hydrogen peroxide as oxidizing agent. The use of synthesized titanium dioxide nanoparticles allowed the highest efficiencies, reaching reductions of 99.4%, 86.0%, and 70.0% for TSS, colour, and COD respectively. GC results showed the reduction of phenol concentrations in 89.7% with our synthesized nanoparticles in contrast to 82.7% reduction, with commercial titanium dioxide nanoparticles.

Synthesis of ZnMn2O4 Nanoparticles by a Microwave-Assisted Colloidal Method and their Evaluation as a Gas Sensor of Propane and Carbon Monoxide.

Spinel-type ZnMn2O4 nanoparticles were synthesized via a simple and inexpensive microwave-assisted colloidal route. Structural studies by X-ray diffraction showed that a spinel crystal phase of ZnMn2O4 was obtained at a calcination temperature of 500 °C, which was confirmed by Raman and UV-vis characterizations. Spinel-type ZnMn2O4 nanoparticles with a size of 41 nm were identified by transmission electron microscopy. Pellet-type sensors were fabricated using ZnMn2O4 nanoparticles as sensing material. Sensing measurements were performed by exposing the sensor to different concentrations of propane or carbon monoxide at temperatures in the range from 100 to 300 °C. Measurements performed at an operating temperature of 300 °C revealed a good response to 500 ppm of propane and 300 ppm of carbon monoxide. Hence, ZnMn2O4 nanoparticles possess a promising potential in the gas sensors field.

Synthesis, Characterization, and Sensor Applications of Spinel ZnCo2O4 Nanoparticles.

Spinel ZnCo2O4 nanoparticles were synthesized by means of the microwave-assisted colloidal method. A solution containing ethanol, Co-nitrate, Zn-nitrate, and dodecylamine was stirred for 24 h and evaporated by a microwave oven. The resulting solid material was dried at 200 °C and subsequently calcined at 500 °C for 5 h. The samples were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and Raman spectroscopy, confirming the formation of spinel ZnCo2O4 nanoparticles with average sizes between 49 and 75 nm. It was found that the average particle size decreased when the dodecylamine concentration increased. Pellets containing ZnCo2O4 nanoparticles were fabricated and tested as sensors in carbon monoxide (CO) and propane (C3H8) gases at different concentrations and temperatures. Sensor performance tests revealed an extremely high response to 300 ppm of CO at an operating temperature of 200 °C.